Performance

It is used as moulds for formatting ceramics and ceramic.

• Freezing period is specially adjusted, and has rapid application feature.

• It is an industrial cast plaster.

Application

Application Areas

It is especially used as adherence master prior to vertical and horizontal gypsum plaster (column, curtain, wall, ceiling, etc.).

Security Warnings

S2: Keep away from reach of children.

Do not store under 5 degrees

Thinning

7 – 7.5 liters of water is added with continuous mixing. Mixing process continues for approx. 3 minutes. In order to maintain rougher surface texture, product might be used without thinning or thinning via low amount of water. No solvent agent or filling should be added except water.

Drying

At least 24 hours at 23 degrees and 50 % relative humidity conditions. It should be noted that drying process shall take more time under dampened and cold environments. It should be noted that environmental dust shall decrease the adhesion and it should not be waited for a long time between applications of primer and plaster applications.

Consumption

It is approximately 0.25 kg/m². Definite consumption should be determined with sampling in site.

Application

By means of its formulation with quartz sand additive, it increases adherence of gypsum and gypsum – lime based liquids to concrete surfaces, and prevents rapid water loss of plaster and thus formation of cracks. It is for use on internal spaces, and is not suggested for usage on dampened and wet surfaces. Application should be implemented as single layer by means of textured rolls. Surfaces, on which Aygips High Adherence Gross Concrete Primer shall be applied, should be clean, solid and free from free particles. Adherence decreasing layers, such as oil, grease, dirt, paint, cement grout, rust, mould grease, concrete curing agents, salt rejection, should be cleaned completely prior to its application. Aygips High Adherence Gross Concrete Primer should be mixed from time to time during application until it reaches to homogenous consistency. Mixing process should absolutely be implemented by means of pin and motorized mixer at low cycle (4000 d/d).